Improved abrasion resistance of textile fabrics due to polymer coatings

Wortmann M, Frese N, Hes L, Gölzhäuser A, Moritzer E, Ehrmann A (2019)
Journal of Industrial Textiles 49(5): 572-583.

Zeitschriftenaufsatz | Veröffentlicht| Englisch
 
Download
Es wurde kein Volltext hochgeladen. Nur Publikationsnachweis!
Autor/in
Wortmann, Martin; Frese, NatalieUniBi; Hes, Lubos; Gölzhäuser, ArminUniBi ; Moritzer, Elmar; Ehrmann, Andrea
Abstract / Bemerkung
Textile fabrics are often subject to abrasion, starting from exposed parts of garments to a variety of technical textiles. Abrasion protection by usual coatings, however, can significantly decrease the water vapor transport through a fabric which is often not desired, especially in the case of garments. In our paper, we report on an approach to combine increased abrasion resistance with sufficient water vapor transport properties. For this, different polymers (poly(methyl methacrylate), acrylonitrile butadiene styrene, or amorphous polyamides) were coated on cotton and polyester woven fabrics. The results of abrasion tests against sandpaper show significantly increased abrasion resistance. The absolute evaporation resistance, measured by a Permetest testing device, was only slightly increased up to values still acceptable for typical garments. Images of all coatings by helium ion microscopy deliver an explanation for the measuring results. Polymer coatings on the polyester fabric resulted in a slight reduction of the hydrophobicity, while coating the cotton fabric severely increased the contact angles of the originally superhydrophilic material.
Stichworte
Coated fabrics; engineered textiles; materials; measurement; protective; fabrics; technical textiles
Erscheinungsjahr
2019
Zeitschriftentitel
Journal of Industrial Textiles
Band
49
Ausgabe
5
Seite(n)
572-583
ISSN
1528-0837
eISSN
1530-8057
Page URI
https://pub.uni-bielefeld.de/record/2937724

Zitieren

Wortmann M, Frese N, Hes L, Gölzhäuser A, Moritzer E, Ehrmann A. Improved abrasion resistance of textile fabrics due to polymer coatings. Journal of Industrial Textiles. 2019;49(5):572-583.
Wortmann, M., Frese, N., Hes, L., Gölzhäuser, A., Moritzer, E., & Ehrmann, A. (2019). Improved abrasion resistance of textile fabrics due to polymer coatings. Journal of Industrial Textiles, 49(5), 572-583. doi:10.1177/1528083718792655
Wortmann, M., Frese, N., Hes, L., Gölzhäuser, A., Moritzer, E., and Ehrmann, A. (2019). Improved abrasion resistance of textile fabrics due to polymer coatings. Journal of Industrial Textiles 49, 572-583.
Wortmann, M., et al., 2019. Improved abrasion resistance of textile fabrics due to polymer coatings. Journal of Industrial Textiles, 49(5), p 572-583.
M. Wortmann, et al., “Improved abrasion resistance of textile fabrics due to polymer coatings”, Journal of Industrial Textiles, vol. 49, 2019, pp. 572-583.
Wortmann, M., Frese, N., Hes, L., Gölzhäuser, A., Moritzer, E., Ehrmann, A.: Improved abrasion resistance of textile fabrics due to polymer coatings. Journal of Industrial Textiles. 49, 572-583 (2019).
Wortmann, Martin, Frese, Natalie, Hes, Lubos, Gölzhäuser, Armin, Moritzer, Elmar, and Ehrmann, Andrea. “Improved abrasion resistance of textile fabrics due to polymer coatings”. Journal of Industrial Textiles 49.5 (2019): 572-583.