We report on the new polycrystalline exchange bias system MnN/CoFe, which shows exchange bias of up to 1800 Oe at room temperature with a coercive field around 600 Oe. The room-temperature values of the interfacial exchange energy and the effective uniaxial anisotropy are estimated to be J(eff) = 0.41 mJ/m(2) and K-eff = 37 kJ/m(3). The thermal stability was found to be tunable by controlling the nitrogen content of MnN. The maximum blocking temperature exceeds 325 degrees C, however the median blocking temperature in the limit of thick MnN is 160 degrees C. Good oxidation stability through self-passivation was observed, enabling the use of MnN in lithographically defined microstructures. As a proof of principle we demonstrate a simple giant magnetoresistance stack exchange biased with MnN, which shows clear separation between parallel and antiparallel magnetic states. These properties come along with a surprisingly simple manufacturing process for the MnN films.