The influence of annealing on temperature dependencies of the magnetoresistivity and resistivity of Fe/Cr multilayers

Lucinski T, Elefant D, Reiss G, vanLoyen L (1997)
phys stat sol (a) 160(1): 133-144.

Download
Es wurde kein Volltext hochgeladen. Nur Publikationsnachweis!
Zeitschriftenaufsatz | Veröffentlicht | Englisch
Autor
; ; ;
Abstract / Bemerkung
Using the thermal treatment for adjusting the giant magnetoresistivity (GMR) values in Fe(3 nm)/Cr(1.1 nm) multilayers, the temperature dependencies of resistivity and magnetoresistivity were examined. A reduction of the residual resistivities after the annealing processes at annealing temperatures lower than 300 degrees C was observed and simultaneously an increase of the magnetoresistivity was noted. Further annealing at higher temperatures degraded gradually the magnetoresistivity. Transport properties were found to be affected by two scattering mechanisms: electron-magnon scattering was dominant for the multilayers exhibiting higher GMR whereas electron-phonon scattering was more pronounced in samples with lower GMR.
Erscheinungsjahr
Zeitschriftentitel
phys stat sol (a)
Band
160
Zeitschriftennummer
1
Seite
133-144
ISSN
eISSN
PUB-ID

Zitieren

Lucinski T, Elefant D, Reiss G, vanLoyen L. The influence of annealing on temperature dependencies of the magnetoresistivity and resistivity of Fe/Cr multilayers. phys stat sol (a). 1997;160(1):133-144.
Lucinski, T., Elefant, D., Reiss, G., & vanLoyen, L. (1997). The influence of annealing on temperature dependencies of the magnetoresistivity and resistivity of Fe/Cr multilayers. phys stat sol (a), 160(1), 133-144. doi:10.1002/1521-396X(199703)160:1<133::AID-PSSA133>3.0.CO;2-H
Lucinski, T., Elefant, D., Reiss, G., and vanLoyen, L. (1997). The influence of annealing on temperature dependencies of the magnetoresistivity and resistivity of Fe/Cr multilayers. phys stat sol (a) 160, 133-144.
Lucinski, T., et al., 1997. The influence of annealing on temperature dependencies of the magnetoresistivity and resistivity of Fe/Cr multilayers. phys stat sol (a), 160(1), p 133-144.
T. Lucinski, et al., “The influence of annealing on temperature dependencies of the magnetoresistivity and resistivity of Fe/Cr multilayers”, phys stat sol (a), vol. 160, 1997, pp. 133-144.
Lucinski, T., Elefant, D., Reiss, G., vanLoyen, L.: The influence of annealing on temperature dependencies of the magnetoresistivity and resistivity of Fe/Cr multilayers. phys stat sol (a). 160, 133-144 (1997).
Lucinski, T, Elefant, D, Reiss, Günter, and vanLoyen, L. “The influence of annealing on temperature dependencies of the magnetoresistivity and resistivity of Fe/Cr multilayers”. phys stat sol (a) 160.1 (1997): 133-144.