Preparation and characterization of gold nanocrystals on NaCl(100) surfaces as labels for the dynamical x-ray tracking technique

Slieh J, Winter A, Gryzia A, Brechling A, Hachmann W, Jacob S, Kandlbinder A, Dietz K-J, Kleineberg U, Heinzmann U (2009)
THIN SOLID FILMS 517(11): 3257-3261.

Journal Article | Published | English

No fulltext has been uploaded

Abstract
We report on the fabrication of single crystalline gold nanocrystals of sizes between 10 nm and 25 nm. Gold was deposited under ultra high vacuum conditions on a freshly-cleaved NaCl(100) surface by means of the Molecular Beam Epitaxy technique. The preparation parameters substrate temperature and average thickness of the deposited gold were studied systematically. After the preparation, the crystals were characterized by means of different techniques, such as Atomic Force Microscopy (AFM), Transmission Electron Microscopy (TEM), X-Ray Diffractometry (XRD) and Laue Diffractometry. Measurements of the deposited cluster size, as measured by AFM, and the crystal size, as measured by XRD exhibited similar results at substrate temperatures between approx. 200 degrees C and 250 degrees C, indicating a high amount of single gold crystals. TEM images of gold crystals, made after the gold crystals had been dissolved in an aqueous 3-[(3-cholamidopropyl)dimethyl-ammonio]propane solution, support these results. Further, an effect of the substrate temperature during the deposition on the orientation of the gold crystals with respect to the NaCl(100) surface was observed. XRD measurements reveal a perpendicular texture of Au (111) parallel to NaCl(001) at approximately 310 degrees C. The second detected texture:Au(001)parallel to NaCl(001) (in plane) and Au[100]parallel to NaCl[100] (perpendicular) was observed over the complete studied temperature range (180 degrees C-330 degrees C). (C) 2008 Elsevier B.V. All rights reserved.
Publishing Year
ISSN
PUB-ID

Cite this

Slieh J, Winter A, Gryzia A, et al. Preparation and characterization of gold nanocrystals on NaCl(100) surfaces as labels for the dynamical x-ray tracking technique. THIN SOLID FILMS. 2009;517(11):3257-3261.
Slieh, J., Winter, A., Gryzia, A., Brechling, A., Hachmann, W., Jacob, S., Kandlbinder, A., et al. (2009). Preparation and characterization of gold nanocrystals on NaCl(100) surfaces as labels for the dynamical x-ray tracking technique. THIN SOLID FILMS, 517(11), 3257-3261.
Slieh, J., Winter, A., Gryzia, A., Brechling, A., Hachmann, W., Jacob, S., Kandlbinder, A., Dietz, K. - J., Kleineberg, U., and Heinzmann, U. (2009). Preparation and characterization of gold nanocrystals on NaCl(100) surfaces as labels for the dynamical x-ray tracking technique. THIN SOLID FILMS 517, 3257-3261.
Slieh, J., et al., 2009. Preparation and characterization of gold nanocrystals on NaCl(100) surfaces as labels for the dynamical x-ray tracking technique. THIN SOLID FILMS, 517(11), p 3257-3261.
J. Slieh, et al., “Preparation and characterization of gold nanocrystals on NaCl(100) surfaces as labels for the dynamical x-ray tracking technique”, THIN SOLID FILMS, vol. 517, 2009, pp. 3257-3261.
Slieh, J., Winter, A., Gryzia, A., Brechling, A., Hachmann, W., Jacob, S., Kandlbinder, A., Dietz, K.-J., Kleineberg, U., Heinzmann, U.: Preparation and characterization of gold nanocrystals on NaCl(100) surfaces as labels for the dynamical x-ray tracking technique. THIN SOLID FILMS. 517, 3257-3261 (2009).
Slieh, J., Winter, Andreas, Gryzia, Aaron, Brechling, Armin, Hachmann, Wiebke, Jacob, S., Kandlbinder, Andrea, Dietz, Karl-Josef, Kleineberg, U., and Heinzmann, Ulrich. “Preparation and characterization of gold nanocrystals on NaCl(100) surfaces as labels for the dynamical x-ray tracking technique”. THIN SOLID FILMS 517.11 (2009): 3257-3261.
This data publication is cited in the following publications:
This publication cites the following data publications:

Export

0 Marked Publications

Open Data PUB

Web of Science

View record in Web of Science®

Search this title in

Google Scholar